CastroI Molub-Alloy™ OG 8031 Range (previously called Molub-Alloy™ 8031) is based on a high viscosity base oil gel formulated with a non-soap, inorganic thickening system. It contains a high viscosity base fluid especially designed to provide Extreme Pressure (EP) and Anti-Wear (AW) characteristics to the lubricant.
A proprietary blend of Molub-Alloy lubricating solids is included to promote anti-wear and load carrying properties. Molub-Alloy lubricating solids work synergistically with chemical reactive AW and EP additives to reduce contact temperatures and wear while providing excellent anti-weld protection under extreme pressure and shock loading.
A proprietary blend of Molub-Alloy lubricating solids is included to promote anti-wear and load carrying properties. Molub-Alloy lubricating solids work synergistically with chemical reactive AW and EP additives to reduce contact temperatures and wear while providing excellent anti-weld protection under extreme pressure and shock loading.
Unit of Measure
Package Type |
N/A Keg |
Weight |
N/A 120 lb |
Appearance |
N/A Dark and Opaque |
Lubricant Composition |
N/A Mineral Oil |
Thickener Type |
N/A Inorganic |
Specific Gravity |
N/A 0.941 |
National Lubricating Grease Institute (NLGI) Consistency |
N/A #00 |
Viscosity at 40 Degree Celsius (ºC) |
N/A 3000 cSt |
Flash Point |
N/A 425 ºF218 ºC |
Penetration at 10 Millimeter (mm) and 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature (Worked 60 Strokes) |
N/A 400 to 430 |
Brookfield Viscosity at 25 Degree Celsius (ºC), Spindle No. 7, 10 rpm |
N/A 80000 cP |
Four Ball Extreme Pressure (EP) Weld Point Load |
N/A 400 kg |
Four Ball Load Wear Index |
N/A 88 kgf |
Copper Corrosion |
N/A 1B |
FZG-Test Failure Load Stage |
N/A > 12 |
US Steel Timken Retention Test |
N/A Pass |
Pumpability by Lincoln Ventmeter at -1 Degree Celsius (ºC) |
N/A 210 psi |
Pumpability by Lincoln Ventmeter at -7 Degree Celsius (ºC) |
N/A 440 psi |
Pumpability by Lincoln Ventmeter at -12 Degree Celsius (ºC) |
N/A 840 psi |
Applications |
N/A
Molub-Alloy OG 8031 is designed to lubricate heavily loaded open gears, screw type actuators, and low to moderate velocity bushings and bearings equipped with centralised or sump type lubrication systems. This Range is recommended for use in open gear applications in cement, mining and any other industries requiring anti-scuff and anti-wear protection, and where no product build up is desired. It is also suited for units containing bushings, bearings and/or gears where ISO 2200, 3000 or 6000 viscosity grade lubricant is required, but straight fluid lubricams leak out. |
Features and Benefits |
N/A
|
Additional Information |
N/A In order to minimise potential incompatibilities when converting to a new grease, all previous lubricant should be removed as much as possible prior to operation. During initial operation, relubrication intervals should be monitored closely to ensure all previous lubricant is purged. |